Wear-resisting POM

Density

Shrinkage

Tensile Strength at break

Elongation at break

Flexural Strength

Flexural Modulus

Izod notched Impact Strength

HDT

Flame rating

Characteristic

Test Method
ASTM

g/cm3

%

MPa

%

MPa

MPa

J/m

℃（1.82MPa）

1.6mm

D792

D955

D638

D638

D790

D790

D256

D648

UL94

M600SS

1.41

1.7-2.2

55

>20

76

2300

80

95

HB

Si Oil modified

M600MS

1.42

1.7-2.2

60

>15

80

2500

60

105

HB

MoS2 filling

M600PT1

1.42

1.8-2.5

53

>15

75

2350

70

103

HB

5%PTFE，general wear-resisting

M600PT2

1.45

1.8-2.2

48

>10

70

2200

60

100

HB

10%PTFE，medium wear-resisting

M600PT3

1.48

1.7-2.1

45

>10

65

2100

45

98

HB

15%PTFE，high wear-resisting

M600PT4

1.52

1.6-2.0

42

>10

63

2000

35

95

HB

20%PTFE，super wear-resisting

M116PT1

1.63

0.4-0.7

100

3

165

7500

55

160

HB

30%GF，5%PTFE filling