Toughening PA6

Density

Shrinkage

Tensile Strength at break

Elongation at break

Flexural Strength

Flexural Modulus

Izod notched Impact Strength

HDT

Flame rating

Characteristic

Test Method
ASTM

g/cm3

%

MPa

%

MPa

MPa

J/m

℃（1.82MPa）

1.6mm

D792

D955

D638

D638

D790

D790

D256

D648

UL94

B500

1.08

1.0-1.4

55

100

85

2100

350

60

HB

general toughening PA6

B580

1.06

1.0-1.4

50

120

55

1800

1000

55

HB

super tougheningPA6

B182

1.17

0.6-1.0

90

5

130

4000

120

185

HB

10%GF,impact modified

B184

1.24

0.5-0.8

110

4

160

5000

180

195

HB

20%GF,impact modified

B186

1.35

0.3-0.5

140

4

200

7500

180

215

HB

30%GF,impact modified

B286

1.31

0.6-1.0

75

6

110

4000

130

95

HB

30% mineral filling,impact modified

B288

1.52

0.4-0.8

65

4

100

5800

60

115

HB

40% mineral filling,impact modified