Toughening PP

MFR

Density

Shrinkage

Tensile Strength at break

Elongation at break

Flexural Strength

Flexural Modulus

Izod notched Impact Strength

HDT

Flame rating

Characteristic

Test Method
ASTM

D1238

g/cm3

%

MPa

%

MPa

MPa

J/m

℃（1.82MPa）

1.6mm

g/10min

D792

D955

D638

D638

D790

D790

D256

D648

UL94

P500

2~4

0.9

1.5-2.0

24

>200

28

1100

150

95

HB

general toughening PP

P580

2~4

0.9

1.5-1.9

20

>200

25

1000

400

80

HB

super tougheningPP

P284

2~4

1.05

1.0-1.2

23

>25

33

2200

120

105

HB

20%Talc filling, toughening

P184CC

6~8

1.04

0.6-0.8

70

4

110

4200

100

160

HB

20%Chemically modified GF,toughened

P186CC

6~10

1.13

0.5-0.7

80

4

115

5500

160

160

HB

30%Chemically modified GF,toughened

P288

8~12

1.24

0.7-0.9

28

>10

50

3100

80

130

HB

40%Talc filling, toughening

P188CC

6~10

1.22

0.3-0.6

90

4

140

6500

170

160

HB

40%Chemically modified GF,toughened